GH1015 is a deformed high-temperature alloy with iron and Fe as the main element. Has good strength and plasticity combination at various temperatures, as well as high thermal strength, good thermal fatigue and oxidation resistance

Delivery :

FOB

minimum order :

100 kilograms

Supply Ability :

5000Tonkilograms / Month

Stock Time :

7-10Day

Country of Origin :

CHINA

Quantity :

Contact Now

GH1015 Features and uses

GH1015 is a deformed high-temperature alloy with iron and Fe as the main element. GH1015 has good strength and plasticity combination at various temperatures, as well as high thermal strength, good thermal fatigue and oxidation resistance; Its stamping, welding and other processes are excellent. There is a phenomenon of aging in long-term use. Parts such as combustion chambers and afterburners for turbo engines operating below 950 ° C

GH1015 Application

This standard is applicable to hot-rolled and forged nickel based and iron-based high-temperature alloy bars used at temperatures ranging from 550 to 1000 ° C. GH1015 can be used to manufacture general load-bearing components for aviation, aerospace, gas turbines, and other industrial purposes (excluding turbine blades)

GH1015 Dimensions and appearance

The dimensions and deviations of GH 2036 and GH 3030 hot-rolled and forged bars shall comply with the provisions of GB 702-72 and GB 908-72, respectively. The dimensions and deviations of other grades of bars should comply with the provisions of Table 1 of this standard; The length and shape of the bar comply with the relevant provisions of the original standard

GH1015 Chemical Element Content (%)

Element	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	W	Nb	B	Ce	Fe
Min	-	-	-	-	-	19	34	-	2.5	4.8	1.1	-	-	Remain
Max	0.08	0.6	1.5	0.02	0.015	22	39	0.25	3.2	5.8	1.6	0.01	0.05	Remain
*B. Ce is added according to the calculated amount.

GH1015 Mechanical Properties

Condition	Heat treatment or condition	Tensile Strength, MPa	Elongation or elongation after fracture, %	Reduction of area , %
Sample (room temperature)*	Heat treatment	≥666.4	≥35	≥40
Sample (700℃)*	Heat treatment	≥392	≥30	≥35
Sample (900℃)*	Heat treatment	≥176.4	≥40	≥45
Sample heat treatment system: 1140-1170 ° C, air-cooled Room temperature mechanical property data measured for heat treated specimens High temperature mechanical performance data measured for heat treated specimens Note:* ① High temperature endurance performance of heat treated specimens: temperature 900 ° C, stress 49 MPa, time ≥ 100 hours.

Lork Group is an supplier of industrial metals to the global aerospace, oil and gas, power generation, petrochemical, bio-medical, pharmaceutical, and other high tech manufacturing industries. Products of premium metal products including Inconel alloys,Incoloy alloys,Monel alloys,Haynes alloys,Hastelloy alloy,stainless steel,China GH Seriesandother superalloy. We certify to most ASME, ASTM, AMS, and military specifications as well as most international standards certification.