Hastelloy X / UNS N06002 / 2.4665 Nickel Alloy
Hastelloy X (W.Nr 2.4665) is a Nickel-Chromium-Iron-Molybdenum alloy with an exceptional combination of oxidation resistance, ease of fabrication and high temperature strength. Lork Group is a premier exporter of premium Hastelloy X alloy products. Request a free quote & sample today.
Delivery :
FOB
minimum order :
50 kilograms
Supply Ability :
5000Tonkilograms / Month
Stock Time :
7-10Day
Country of Origin :
CHINA
Quantity :
Hastelloy X (W.Nr 2.4665) is a Nickel-Chromium-Iron-Molybdenum alloy with an exceptional combination of oxidation resistance, ease of fabrication and high temperature strength. UNS N06002 alloy exhibits good ductility after prolonged exposure at temperatures of 1200, 1400, and 1600°F (650, 760, and 870°C) for 16,000 hours. Alloy X possesses exceptional strength and oxidation resistance up to 1200°C (2200°F), and has exceptional forming and welding characteristics. Some applications that Hastelloy X is recommended for includes gas turbine engines, combustor cans, spray bars and flame holders.
Hastelloy X nickel alloy is available in the form of plates, sheets, strips, billets, bars, wires, pipes, tubes, and covered electrodes. Please get in touch with the sales department of Lork Group for more product information and quotations.
Chemical Composition
| Element | Content (%) |
|---|---|
| Cr, Chromium | 20.5-23 |
| Fe, Iron | 17-20 |
| Mo, Molybdenum | 8-10 |
| Mn, Manganese | 1 max |
| Si, Silicon | 1 max |
| Ti, Titanium | 0.15 max |
| Co, Cobalt | 0.5-2.5 |
| Al, Aluminum | 0.5 max |
| Cu, Copper | 0.5 max |
| C, Carbon | 0.05-0.15 |
| P, Phosphorus | 0.04 max |
| S, Sulfur | 0.03 max |
| W, Tungsten | 0.2-1 |
| B, Boron | 0.008 max |
| Ni, Nickel | Remainder |
Physical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Density | 8.220 g/cm³ | 0.297 lb/in³ |
| Melting point | 1316°C | 2400°F |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 755 MPa | 109.5 Ksi |
| Yield strength | 385 MPa | 55.9 Ksi |
| Elastic modulus | 205 GPa | 29.8 psi |
| Reduction of area | 22% | 22% |
| Hardness, Rockwell B (converted from Brinell hardness) | 87 | 87 |
Thermal Properties
| Properties | Metric | Imperial |
|---|---|---|
| Thermal expansion co-efficient | 13.0 µm/m°C | 7.2 µin/in°F |
| Thermal conductivity | 9.1 W/mK | 63 BTU in/hr.ft².°F |
Heat-Treatment
Wrought forms of Hastelloy X alloy are furnished in the solution heat-treated condition unless otherwise specified. X alloy is typically solution heat-treated at 2150°F (1177°C) and rapid cooled. Bright annealed products are cooled in hydrogen. Annealing at temperatures lower than the solution heat- treating may cause precipitation of secondary phases, which may affect the alloy’s strength and ductility.
Welding
The alloy can be welded by a variety of techniques, including gas tungsten arc (GTAW), gas metal arc (GMAW), shielded metal arc (SMAW), and resistance welding.